Boron doses of 1×1012–5×1015/cm2 were implanted at 60 keV into 1-μm-thick polysilicon films. After annealing at 1100 °C for 30 min, Hall and resistivity measurements were made over a temperature range −50–250 °C. It was found that as a function of doping concentration, the Hall mobility showed a min...