Polycrystalline bulk samples of Ti 3 SiC 2 were fabricated by reactively hot‐pressing Ti, graphite, and SiC powders at 40 MPa and 1600°C for 4 h. This compound has remarkable properties. Its compressive strength, measured at room temperature, was 600 MPa, and dropped to 260 MPa at 1300°C in air. Alt...